ANYCUBIC PLA-CF IPHPFFW-101 is a carbon fiber-reinforced filament that combines the aesthetic appeal of multicolored prints with high mechanical strength. The addition of carbon fiber reduces layer visibility, resulting in a more uniform surface and a better visual effect for models such as mechanical structures or vehicles. The matte finish gives prints a professional look without the need for additional post-processing, saving time and simplifying the creation process.

The material was designed for increased strength and resistance to deformation compared to standard PLA Matte. The material’s stiffness of 3100 MPa confirms its durability, making it suitable for more demanding applications. Low material shrinkage minimizes the risk of deformation, resulting in high dimensional accuracy and excellent print quality, particularly in parts requiring precise fit.

The filament is easy to use and compatible with desktop printers, offering a smooth printing process and minimal risk of nozzle clogging (use of a hardened steel nozzle is recommended). A built-in chip enables smart material identification in the Anycubic ACE Pro system, allowing for automatic adjustment of print settings (requires an internet connection and compatible devices). This solution simplifies the workflow and reduces the need for manual configuration.

The filament comes with a reusable spool featuring a threaded connection system, which increases stability and reduces the risk of material tangling. The design is heat-resistant up to 100°C, ensuring durability during use. Additionally, the product was designed with reuse and a more environmentally friendly approach in mind.

| Manufacturer | Anycubic |
|---|---|
| Model | IPHPFFW-101 |
| Material | PLA-CF |
| Weight | 1 kg |
| Color | white |
| Curing | recommended (55°C for 6–8 hours) |
| Recommended nozzle diameter | ≥ 0.4 mm |
| Nozzle temperature | 210–250°C |
| Bed temperature | 55–70°C |
| Recommended print speed | 40–250 mm/s |
| Maximum flow rate | 20 mm³/s |
| Density | 1.22 g/cm³ |
| Melting point | 165°C |
| Vicat softening temperature | 69°C |
| Heat deflection temperature | 60°C |
| Tensile strength | 44 ± 3 MPa |
| Elongation at break | 10.5 ± 1.5% |
| Flexural strength | 74 ± 5 MPa |
| Impact resistance (Izod) | 25 ± 2 kJ/m² |