Name: ANYCUBIC ABS-Like Resin 3.0, čierna
Brand: AnyCubic
SKU: 131186
Price: 26.9 EUR
Availability: InStock

-5%

Novinka

AnyCubic

26,90 €25,56 €

Cena bez DPH 20,78 €

-5%

Zľava s kupónom EXTRA3D

Na sklade > 5 ks

Doručenie už 10. septembra

Doprava už od 3,90 € (Zadarmo od 50,00 €)

Prečo nakupovať u nás ?

14 rokov na trhu

30 dní na vrátenie

825024+ vybavených objednávok

5000+ výdajných miest

Výrobca

AnyCubic

Produktové číslo

SABL3BK-10-IPO-01

EAN

6974662352262

Elektronika 3D Tlač 3D Tlačiarne príslušenstvo

AIOpýtať sa na produkt

Popis a špecifikácia
Recenzie (0)

ANYCUBIC ABS-Like Resin 3.0 (black)

ANYCUBIC ABS-Like Resin 3.0 is a photopolymer resin designed for LCD and DLP 3D printers, combining high mechanical strength, crack resistance, and high print accuracy. With an elongation at break of 25–30%, an impact strength of 130 J/m, and a low volumetric shrinkage rate (3.9–4.9%), it allows you to create durable models with a smooth surface and a very high level of detail. Low viscosity and minimal odor further enhance working comfort.

A dark bottle of Anycubic ABS-Like Resin 3.0 Black stands next to a black figurine of a samurai riding a horned creature

Greater flexibility and improved strength

ABS-Like Resin 3.0 is ideal for creating parts subjected to stress. With a hardness of 83–86 HD and high impact resistance, the finished models retain their durability even during drilling and further machining. The material also stands out for its very low susceptibility to warping, making it ideal for printing mechanical parts, device enclosures, and automotive components. Additionally, ABS-Like Resin 3.0 offers an elongation at break of up to 30%, which is nearly twice that of many standard ABS-type resins. These properties allow the material to better withstand stress and increase the models’ resistance to damage caused by everyday use.

A comparison of using a gray hammer to drive a nail and a screwdriver to tighten a screw in a plastic angle bracket

High precision and shorter print times

Low shrinkage and an optimally selected viscosity of 280–300 mPa·s result in highly accurate detail reproduction and a smooth surface texture. The material’s good flow accelerates its return to the build volume, which helps reduce print time and increase productivity.

A black samurai figurine with a sword and a flag, riding a horned creature, set against a light background

Comfort during printing and broad compatibility

The resin formula was developed to minimize odor and reduce the risk of irritation during use. You also don’t have to worry about compatibility issues—ABS-Like Resin 3.0 works with a wide range of LCD and DLP 3D printers that use UV light with a wavelength between 365 and 405 nm. This makes it ideal for both home workshops and more advanced projects.

A row of Anycubic ABS-Like Resin 3.0 bottles and their corresponding colored figurines on a desk

Manufacturer	ANYCUBIC
Model	ABS-Like 3.0
Color	Black
Material	Photopolymer resin
Wavelength	365–405 nm
Viscosity	280–300 mPa·s (25°C)
Density	1.06–1.09 g/cm³
Hardness	83–86 HD
Tensile strength	38–45 MPa
Elongation at break	25–30%
Flexural modulus	50–65 MPa
Flexural strength	1500–2000 MPa
Young’s modulus	1300–1700 MPa
Izod impact strength	130 J/m
Volumetric shrinkage	3.9–4.9%
Printing temperature	20–50°C
Recommended ambient temperature during printing	20–40°C
Exposure time for the first layer	23–40 s
Exposure time for a standard layer	2–3.6 s
Cleaning agent	95% IPA
Washing time	≥3 min
UV wavelength during curing	405 nm
Curing temperature	18–30°C
UV irradiance	25,000–30,000 µW/cm²
Curing time	3 min